high-reliability power inductors ml414pjb 3314 power inductors document ml541-1 revised 09/24/12 inductance dcr isat (a) 5 irms (a) 6 20% 2 max 3 srf (mhz) 4 10% 20% 30% 20c 40c part number 1 (h) (ohms) min typ drop drop drop rise rise ml414pjb102mlz 1.0 0.055 150 215 1.8 1.9 1.9 1.3 1.7 ml414pjb222mlz 2.2 0.100 98.0 140 1.1 1.4 1.5 0.96 1.3 ml414pjb332mlz 3.3 0.145 80.5 115 0.98 1.2 1.3 0.80 1.1 ml414pjb472mlz 4.7 0.175 60.2 86 0.97 0.99 1.0 0.72 1.0 ml414pjb562mlz 5.6 0.220 51.8 74 0.92 0.95 0.98 0.66 0.88 ml414pjb682mlz 6.8 0.240 50.4 72 0.82 0.83 0.86 0.66 0.88 ml414pjb822mlz 8.2 0.270 42.0 60 0.58 0.75 0.78 0.56 0.80 ml414pjb103mlz 10 0.330 38.5 55 0.56 0.66 0.70 0.52 0.70 ml414pjb153mlz 15 0.440 31.5 45 0.46 0.56 0.59 0.50 0.66 ml414pjb183mlz 18 0.575 25.9 37 0.44 0.51 0.54 0.42 0.54 ml414pjb223mlz 22 0.720 23.8 34 0.44 0.48 0.49 0.36 0.48 ml414pjb333mlz 33 0.920 18.9 27 0.30 0.38 0.40 0.34 0.46 ml414pjb473mlz 47 1.40 15.4 22 0.28 0.33 0.34 0.28 0.38 ml414pjb563mlz 56 1.55 13.3 19 0.26 0.30 0.31 0.26 0.34 ml414pjb683mlz 68 1.80 11.9 17 0.22 0.26 0.29 0.24 0.32 ml414pjb823mlz 82 2.00 9.8 14 0.20 0.24 0.26 0.23 0.31 ml414pjb104mlz 100 2.75 9.1 13 0.19 0.23 0.24 0.21 0.30 ml414pjb124mlz 120 3.45 7.7 11 0.19 0.21 0.22 0.18 0.24 ml414pjb154mlz 150 4.10 7.0 10 0.16 0.19 0.20 0.16 0.22 ml414pjb184mlz 180 4.80 6.3 9.0 0.14 0.17 0.18 0.15 0.20 ml414pjb224mlz 220 6.00 4.90 7.0 0.14 0.16 0.17 0.13 0.18 ml414pjb334mlz 330 9.30 4.20 6.0 0.11 0.12 0.13 0.10 0.14 ml414pjb474mlz 470 12.0 3.15 4.5 0.080 0.11 0.11 0.10 0.13 ml414pjb564mlz 560 14.0 3.15 4.5 0.095 0.105 0.11 0.090 0.12 ml414pjb684mlz 680 18.5 2.80 4.0 0.092 0.100 0.105 0.080 0.10 ml414pjb824mlz 820 24.0 2.59 3.7 0.086 0.099 0.100 0.070 0.090 ml414pjb105mlz 1000 31.0 2.10 3.0 0.090 0.099 0.100 0.065 0.080 ml414pjb155mlz 1500 44.0 1.89 2.7 0.080 0.086 0.090 0.050 0.060 core material ferrite terminations silver-palladium-platinum-glass frit. weight 44.1 C 46.5 mg ambient temperature C55c to +105c with i rms current, +105c to +155c with derated current storage temperature component: C55c to +155c. tape and reel packaging: C55c to +80c resistance to soldering heat max three 40 second refows at +260c, parts cooled to room temperature between cycles moisture sensitivity level (msl) 1 (unlimited foor life at <30c / 85% relative humidity) enhanced crush-resistant packaging 1000/7reel plastic tape: 12 mm wide, 0.3 mm thick, 8 mm pocket spacing, 1.52 mm pocket depth recommended pick and place nozzle od: 3.3 mm; id: 1.65 mm high temperature material allows operation in ambient temperatures up to 155c special construction allows it to pass vibration testing to 80 g and shock testing to 1000 g. 1. when ordering, please specify testing code: ml414pjb105mlz testing: z = cots h = screening per coilcraft cp-sa-10001 n = screening per coilcraft cp-sa-10004 2. inductance tested at 100 khz, 0.1 vrms using an agilent/hp 4192a. inductance at 1 mhz is the same for parts with srf 10 mhz. 3. dcr measured on a micro-ohmmeter. 4. srf measured using agilent/hp 8753es or equivalent. 5. dc current that causes the specifed inductance drop from its value without current. 6. current that causes the specifed temperature rise from 25c ambient. 7. electrical specifcations at 25c. refer to doc 362 soldering surface mount compo - nents before soldering. ? ? coilcraft, inc. 2012 1102 silv er lak e road car y, il 60013 phone 800-981-0363 fa x 847-639-1508 email c ps@coilcraft.com www . coilcraft-cps . com this pr oduct may not be used in medical or hig h risk applications without prior coilcraft appr oval. specifications subject to change without notice. please check our web site for latest infor mation.
ml414pjb series (3315) 3314 power inductors typical l vs current typical l vs frequency 0.01 0.1 11 0 current (a) 0. 1 1 10 10000 1000 100 inductance (h) 1 h 10 h 3.3 h 33 h 100 h 330 h 1000 h 0.01 0.1 11 0 frequency (mhz) 0. 1 1 10 10000 1000 100 inductance (h) 1 h 10 h 3.3 h 33 h 100 h 330 h 1000 h current derating dimensions are in inches mm -40 -55 -20 02 04 06 08 0 100 160 140 120 ambient temperature (c) pe r cent of rated current 120 110 100 90 80 70 60 50 40 30 20 10 0 25c i sat i rm s document ml541-2 revised 09/24/12 ? ? coilcraft, inc. 2012 1102 silv er lak e road car y, il 60013 phone 800-981-0363 fa x 847-639-1508 email c ps@coilcraft.com www . coilcraft-cps . com this pr oduct may not be used in medical or hig h risk applications without prior coilcraft appr oval. specifications subject to change without notice. please check our web site for latest infor mation.
|
